Microsc. Microanal. Microstruct. 1, 103-108 (1990)
DOI: 10.1051/mmm:0199000102010300

STM of CrCl3-graphite intercalation compounds

Philippe Biensan, Jean-Claude Roux, Hassan Saadaoui et Serge Flandrois

Centre de Recherche Paul Pascal, Château Brivazac, 33600 Pessac, France

Abstract
Scanning tunneling microscopy has been used to image stage-2 CrCl 3-graphite intercalation compounds with atomic resolution. Images obtained after cleaving the samples are characteristic of two types of domains. One (the most frequent) exhibits an hexagonal lattice where all carbon atoms are equivalent, whereas the other shows a centered hexagonal structure similar to that of pristine graphite. These two domains can be related to Daumas-Herold domains with one and two graphite layers, respectively, covering the guest layer closest to the surface.

Résumé
La microscopie à effet tunnel a été utilisée pour étudier les composés d'insertion graphite-CrCl3 de stade-2. Les images obtenues de la surface après clivage sont caractéristiques de deux types de domaines. Le plus fréquent apparaît sous forme d'un plan de structure hexagonale dont tous les atomes de carbone sont équivalents, tandis que l'autre montre une structure hexagonale centrée proche de celle du graphite pur. Ces deux types de domaines peuvent être reliés aux domaines de Daumas-Herold avec un et deux plans de graphite, respectivement, recouvrant le plan intercalé le plus proche de la surface.

PACS
6837E - Scanning tunneling microscopy (including chemistry induced with STM).
6835B - Structure of clean surfaces (reconstruction).

Key words
STM -- Surface structure -- Cleavage -- Domain structure -- Graphite intercalation compounds -- Chromium chlorides