Microsc. Microanal. Microstruct. 5, 203-211 (1994)
DOI: 10.1051/mmm:0199400503020300

TEM investigation of iron segregation modes in CuAlFe dilute alloys

A. Hauet, A. Bigot et D. Blavette

Paculté des Sciences de Rouen, URA 808, 76821 Mont Saint Aignan Cedex, France

Abstract
Iron has a very low solubility in copper (a few % at 1000 °C) as well as in the α solid solution of the Cu-Al alloy. We describe here the iron segregation modes which are observed during the slow cooling of the α (FCC) and β (BCC) solid solutions of CuAlFe alloys containing about 10 wt% Al and 4% Fe. At high temperature iron at first precipitates into α or r Fe; then at lower temperature iron-rich phases are observed containing also Cu and Al. Particularly, the α2 phase appears very quickly, and it is thought to be richer in Fe than the α matrix.

Résumé
La solubilité du fer dans le cuivre est très faible (quelques % à 1000 °C), et on sait qu'elle demeure faible dans la solution solide α de cuivre aluminium. Nous décrivons ici les modes de ségrégation du fer observés au cours du refroidissement lent des solutions solides α (CFC) et β (CC) d'alliages ternaires CuAlFe de teneurs en Al proches de 10% mass. et contenant 4% Fe. A haute température, le fer a d'abord tendance à ségréger en fer α ou en fer r ; lorsque la température diminue, on observe la précipitation de phases riches en fer, mais contenant aussi du cuivre et de l'aluminium. Nous montrons en particulier que la phase stable α 2 se forme trés vite, et nous pensons qu'elle est plus riche en fer que la matrice α.

PACS
6475 - Solubility, segregation, and mixing.
8130M - Precipitation.

Key words
aluminium alloys -- cooling -- copper alloys -- dilute alloys -- iron alloys -- precipitation -- segregation -- transmission electron microscopy -- CuAlFe -- dilute alloys -- segregation modes -- slow cooling -- precipitates -- TEM -- 1000 C